Introduction
AISI 321/JIS SUS321 Austenite heat resistant stainless steel bar.
Type 321 stainless steel is Ni - Cr – Ti austenitic stainless steel, its performance is very similar with 304, but due to join the metal titanium, make it have better grain boundary corrosion resistance and high temperature strength. Because of adding titanium, make its effective control the formation of chromium carbide.
321 stainless steel has excellent high temperature Stress Rupture (Stress Rupture) properties and high temperature Creep Resistance (Creep to hold) Stress and mechanical properties are better than that of 304 stainless steel.
Standards: ASTM, JIS, GB, EN (DIN, BS, NF) Or Per as clients’ requires.
Product Basic Information:
Material | ASTM 321 | ||
Chemical Composition | Mechanical Properties(In Quenched & Tempered State) 565 °C | ||
C | <> | Tensile strength(MPA) | 205 |
Si | <> | Yield strength (MPA) | 540 |
Mn | <> | Elongation(δ5/%) | 40 |
Cr | 17.00-19.00 | Reduction in Area (ψ/%) | 50 |
Mo | - | Impact (J)v | -- |
P | ≤0.035 | Hardness | <> |
S | ≤0..030 | ||
N | 0.35-0.50 | ||
Ni | 8.00-11.00 | ||
Similar steel grade & equivalent steel materials:
USA | Japanese | Gemany | British | France | International | Chinese |
ASTM&AISI&SAE | JIS | EN DIN | EN BS | EN NF | ISO | GB |
321 | SUS321 | X6CrNiTi18-10(1.4541) | ------ | 1Cr18Ni9Ti |
Seamless steel pipe process：
The production process of general seamless steel tubes can be divided into two types: cold-drawn and hot-rolled. The production process of cold-rolled seamless steel tubes is generally more complicated than hot-rolled. The tube blank must first be subjected to three-roll continuous rolling, and then extruded. In the sizing test, if the surface does not respond to cracks, the round pipe is cut by a cutter and cut into a blank of about one meter in length. Then enter the annealing process. Annealing must be acid-washed with an acidic liquid. When pickling, pay attention to whether there is a large amount of blistering on the surface. If there is a large amount of blistering, the quality of the steel pipe cannot meet the response standard. The appearance of cold-rolled seamless steel pipe is shorter than that of hot-rolled seamless steel pipe. The thickness of cold-rolled seamless steel pipe is generally smaller than that of hot-rolled seamless steel pipe, but the surface looks brighter than thick-walled seamless steel pipe. It's rough, and it doesn't have too much burr. The hot-rolled seamless steel pipe is generally delivered in the hot-rolled state after heat treatment. Hot-rolled seamless steel pipes are subject to strict manual selection by the staff after quality inspection. After the quality inspection, the surface is oiled, followed by multiple cold-drawing experiments. After the hot-rolling treatment, a perforation experiment is performed. If the diameter of the perforation is too large, straightening correction is required. After straightening, it is transferred to the flaw detector by the conveying device for flaw detection experiments. Finally, the labels are labeled and the specifications are arranged and placed in the warehouse.